| Tested to |
EN ISO 14411 standart:
Annex G, dry pressed ceramic tiles of low water absorption from group BIa (Eb ≤ 0.5%) Tests carried out in compliance with the EN ISO 10545 standard section 1–16. | CE | ||||
|---|---|---|---|---|---|---|
| Sizing | Length and Width | Acceptable difference between the average dimension of each tile and the manufacturing size |
-0.38 mm ~ -0.12 mm -0.25 % ~ -0.08 % |
± 0.6 % and ± 2.0 mm | EN ISO 10545-2 |
|---|---|---|---|---|---|
| Thickness | Acceptable difference between the average thickness of each tile and the production thickness |
-0.39 mm ~ -0.29 mm -4.3 % ~ -3.2 % |
± 5 % and ± 0.5 mm | ||
| Side straightness | Maximum acceptable straightness difference compared to the manufacturing sizes |
0.05 mm ~ 0.35 mm 0.03 % ~ 0.23 % |
± 0.5 % and ± 1.5 mm | ||
| Angularity | Maximum acceptable angularity difference compared to the manufacturing sizes |
0.05 mm ~ 0.55 mm 0.03 % ~ 0.36 % |
± 0.5 % and ± 2.0 mm | ||
| Surface quality | Minimum percentage of tiles without visible defects from the manufactured sample | 100 % | A minimum of 95% of the tiles shall be free from visible defects | ||
| Breaking strength | Bending breaking load | 52 | Minimum 35 N/mm² individual | EN ISO 10545-4 | |
| Breaking strength | 2152 |
Thickness ≥ 7.5 mm Not less than 1300 N |
|||
| Thermal shock resistance | No visible defects after 10+ times of thermal shock cycles | EN ISO 10545-9 | |||
| Frost resistance | No visible defects after 100 freeze cycles | EN ISO 10545-12 | |||
| Chemical resistance | Low concentration acids and bases | Class A | EN ISO 10545-13 | ||
| High concentration acids and bases | |||||
| Stain resistance | Variety of common staining agents of various viscosity | Class 5 | EN ISO 10545-14 | ||
| Slipperiness | Slider type: type 96 (4S rubber) – Dry condition | 62 | CEN/TS 16165 | ||
| Slider type: type 96 (4S rubber) – Wet condition | 54 | ||||
| Anti-slipperiness | Bare feet | B | DIN 51097 | ||
| Footwear | R10 | DIN 51130 | |||
| Water drainage volume | V8 | DIN 51130 | |||